What is 1100 aluminum used for?
Applications. Aluminium / Aluminum 1100 alloy is widely used in fin stock, heat exchanger fins, spun hollowware, dials and name plates, decorative parts, giftware, cooking utensils, rivets and reflectors, and in sheet metal work.
How strong is 1100 aluminum?
Aluminum 1100
| Properties | Metric | English |
|---|---|---|
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi |
| Elongation at Break | 15 – 28% | 15 – 28% |
| Modulus of Elasticity | 68.9 GPa | 103000 ksi |
Is 1100 heat-treatable?
Aluminum 1100: This is commercially pure aluminum, 99% min pure. It is soft, ductile, and has excellent workability which makes it ideal for projects requiring challenging forming operations. It work-hardens slowly, and is not heat-treatable.
Can you heat treat 1100 aluminum?
Aluminum 1100 is just one of several common aluminum alloys and is soft, low strength and, at 99% min aluminum, is the commercially pure aluminum. Copper, iron, magnesium, manganese, silicon, titanium, vanadium and zinc comprise the remaining elements. It cannot be hardened by heat treatment and is very formable.
What are the different types of aluminum?
Different Aluminum Grades Aluminum comes in three basic types: 1100, 3003, and 6061. The grade of the aluminum will determine the end-use application and price point. For example, 1100 is a lower-cost material than 6061 but cannot be used for high-temperature applications like cooking utensils or pot lids.
What is ASTM B209?
ASTM B209-10. November 1, 2010. Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate. 1.1 This specification covers aluminum and aluminum-alloy flat sheet, coiled sheet, and plate in the alloys (Note 1) and tempers shown in Tables 2 and 3, in the following finishes: 1.1.1 Plate in…
What is best grade of aluminum?
5052 aluminum is the highest strength alloy of the more non-heat-treatable grades. Its resistance to fatigue is better than most grades of aluminum. Alloy 5052 has a good marine atmosphere corrosion resistance of saltwater and excellent workability.